| Monolayer thickness, mm | GOST R 56682 | 0.16 |
| Tensile strength σ11+, MPa at 25°C | GOST R 56785 | 2037 |
| Tensile modulus of elasticity E11+, GPa at 25°C | GOST R 56785 | 151 |
| Compressive strength σ11-, MPa at 25°C | GOST 56812 | 1088 |
| Shear strength τ13, MPa at 25°C | GOST 32659 | 82 |
| Shear strength τ13, MPa at 85°C | GOST 32659 | 57 |
| In-plane shear strength τ12, MPa at 25°C | GOST R 56799 | 66 |
| In-plane shear strength τ12, MPa at 85°C | GOST R 56799 | 50 |
| Tensile strength [+45/0/-45/90]3S, σ11+, MPa at 25°C | GOST R 56785 | 692 |
| Tensile modulus [+45/0/-45/90]3S, E11+, GPa at 25°C | GOST R 56785 | 53 |
| Compressive strength [+45/0/-45/90]3S, σ12-, MPa at 25°C | GOST 56812 | - |
| Shear strength [+45/0/-45/90]3S, τ13, MPa at 25°C | GOST 32659 | 53 |
| Shear strength [+45/0/-45/90]3S, τ13, MPa at 85°C | GOST 32659 | 45 |
| In-plane shear strength [+45/0/-45/90]3S, τ12, MPa at 25°C | GOST R 56799 | 231 |
| In-plane shear strength [+45/0/-45/90]3S, τ12, MPa at 85°C | GOST R 56799 | 283 |
| Charring length, avg., mm | 60 |
| Burning time, avg., sec | 1 |
| Burning of a drop separating from a test sample after falling on average, avg., sec | 0 |