Epoxyphenolic prepreg ITM180/SW60A

Nominal density of reinforcing filler, g/m2

60
Binder content, %

36
Monolayer thickness, mm

0.05
Glass transition temperature, ℃

140
Density, g/cm3

1.9
T hole, °C

130℃ (120 min)/150℃ (10 min)
Operating temperature, °C

85
Type of binder

Epoxyphenolic
Reinforcing filler

Glass fabric SW60A (60 g/m2)

from 2 760 ₽/m²

excluding VAT

from 3 367 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

Epoxy-phenolic prepreg ITM180 is suitable for the manufacture of interior trim for aircraft cabins, interior ceiling and wall panels, as well as for lining cargo and baggage compartments.

Applies:

from 2 760 ₽/m²

excluding VAT

from 3 367 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

Other prepregs

T hole, °C:
130℃ (120 min)/150℃ (10 min)
Operating temperature, °C:
85
Type of binder:
Epoxyphenolic
Reinforcing filler:
200g/m2 carbon unidirectional tape

T hole, °C:
130℃ (120 min)/150℃ (10 min)
Operating temperature, °C:
85
Type of binder:
Epoxyphenolic
Reinforcing filler:
carbon unidirectional tape 160 g/m2

T hole, °C:
130℃ (120 мин)/150℃ (10 мин)
Operating temperature, °C:
85
Type of binder:
Эпоксифенольный
Reinforcing filler:
углеродная однонаправленная лента 120 г/м2

T hole, °C:
130℃ (120 мин)/150℃ (10 мин)
Operating temperature, °C:
85
Type of binder:
Эпоксифенольный
Reinforcing filler:
стеклоткань С280, 280 г/м2

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

+7 (495) 133-26-78

for product purchasing inquiries

sales@itecma.ru

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

info@cspekt.ru

production and warehouse

Podolsk, Zavodskaya St., Building 2

head office

Moscow, Ramensky Boulevard, Building 1

Website creation – NetLab

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Nominal density of reinforcing filler, g/m2	GOST 32649	60
Binder content, %	GOST 56796	36
Monolayer thickness, mm	GOST R 56682	0.05
Glass transition temperature, ℃	GOST R 57739	140
Tensile strength, MPa 25℃	GOST R 56785	562
Tensile modulus of elasticity, GPa at 25℃	GOST R 56785	22
Compressive strength, MPa 25℃	GOST R 56812	406
Shear strength, MPa 25℃	GOST 32659	57
Density, g/cm3	GOST 15139	1.9

Epoxyphenolic prepreg ITM180/SW60A

Key Features

Scope of application

Storage and transportation conditions

Application