Compressive strength 0° σ11-, MPa at 25°C (curing at RT)
25
Compressive strength 0° σ11-, MPa at 25°C (curing at 140°C)
0.65-0.7
Density, g/cm3
0.65-0.7
T hole, °C
25℃ (24 h)/65℃ (2 h)
Operating temperature, °C
85
Compressive strength, MPa
33
from 5 500 ₽/kg
excluding VAT
from 6 710 ₽/kg
with 22% VAT
Minimum order quantity -
5 kg.
Not a public offer
Epoxy-phenolic interior paste ITM25 is designed for filling honeycombs and sealing the ends of three-layer honeycomb panels used for the production of interior ceiling and wall panels for cargo and baggage compartments of aircraft.
ITM25 epoxy-phenolic paste is designed for filling honeycombs and sealing the ends of three-layer honeycomb panels used for cabin interiors, interior ceiling panels, and walls of aircraft cargo and baggage compartments. This increases their rigidity and allows for repairs.
Paste ITM25 complies with Part I and Part III of Appendix F of AP-25 as part of the design.
Key Features
Does not support combustion
Low moisture absorption
Low smoke emission
Operating temperature from -60 to 85℃
Forming mode
Room temperature curing: keep at room temperature 17-30°C for at least 24 hours.
Baking: holding at 65°C for at least 2 hours.
Storage
The paste components are stored and transported in their original packaging, upright, with the lid facing up, at temperatures up to +40°C. The lower temperature limit is determined by the container used:
Polymer containers not below -27℃
Metal containers not below -40℃
The paste components are transported by all types of covered transport, ensuring the required temperature conditions and protection from mechanical impact.