Foaming film adhesive bismaleimide AMV250

Film thickness, mm

0.90±0.09
Tensile strength at peeling of skin from honeycomb core made of AMG-2N foil 0.03-0.04 mm thick with a cell size of 2.5 mm at a temperature of 25 °C, MPa, not less

2
Tensile strength of skin from honeycomb core made of AMG-2N foil 0.03-0.04 mm thick with a cell size of 2.5 mm at a temperature of 250 °C, MPa, not less

2
Surface density, g/m2

1000±100
Glass transition temperature °C, not less

160
T hole, °C

230
Operating temperature, °C

250
Shear strength, MPa

-

from 38 000 ₽/m²

excluding VAT

from 46 360 ₽/m²

with 22% VAT

Minimum order quantity -

Not a public offer

AMV250 is a film-type foaming bismaleimide adhesive for bonding honeycomb structures operated at temperatures from -60°C to +250°C.

Applies:

from 38 000 ₽/m²

excluding VAT

from 46 360 ₽/m²

with 22% VAT

Minimum order quantity -

Not a public offer

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

for product purchasing inquiries

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

production and warehouse

head office

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Film thickness, mm	0.90±0.09
Tensile strength at peeling of skin from honeycomb core made of AMG-2N foil 0.03-0.04 mm thick with a cell size of 2.5 mm at a temperature of 25 °C, MPa, not less	2
Tensile strength of skin from honeycomb core made of AMG-2N foil 0.03-0.04 mm thick with a cell size of 2.5 mm at a temperature of 250 °C, MPa, not less	2
Surface density, g/m2	1000±100
Glass transition temperature °C, not less	160