Prepreg VNT120T/UD120

Monolayer thickness, mm

0.12
Tensile strength, MPa 25℃

2135
Compressive strength, MPa 25℃

1135
Density, g/cm3

1.52
Punch ratio

0.392
T hole, °C

130℃ (120 min)/150℃ (15 min)
Operating temperature, °C

100
Type of binder

Epoxy
Reinforcing filler

120g/m2 carbon unidirectional tape
Width, mm

1000

from 4 700 ₽/m²

excluding VAT

from 5 734 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

VNT120T is a prepreg based on an epoxy binder with a low curing temperature and carbon reinforcing fillers. It can be processed in both autoclave and non-autoclave conditions for the manufacture of components operating at temperatures up to 85°C. It can be cured in conjunction with the ITEKMA epoxy system.

Applies:

from 4 700 ₽/m²

excluding VAT

from 5 734 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

Other epoxy - curing 130°c

T hole, °C:
130℃ (120 мин)/150℃ (15 мин)
Operating temperature, °C:
100
Type of binder:
Эпоксидный, 38%
Reinforcing filler:
углеродная ткань саржа 2/2 200 г/м2
Width, mm:
1000

T hole, °C:
130℃ (120 мин)/150℃ (10 мин)
Operating temperature, °C:
100
Type of binder:
Эпоксидный, 40%
Reinforcing filler:
арамидная ткань 400 г/м2
Width, mm:
1000

T hole, °C:
130℃ (120 min)/150℃ (15 min)
Operating temperature, °C:
100
Type of binder:
Epoxy
Reinforcing filler:
200g/m2 carbon unidirectional tape
Width, mm:
1000

T hole, °C:
130℃ (120 min)/150℃ (15 min)
Operating temperature, °C:
100
Type of binder:
Epoxy
Reinforcing filler:
fiberglass E-3/1-100
Width, mm:
1000

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

+7 (495) 133-26-78

for product purchasing inquiries

sales@itecma.ru

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

info@cspekt.ru

production and warehouse

Podolsk, Zavodskaya St., Building 2

head office

Moscow, Ramensky Boulevard, Building 1

Website creation – NetLab

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Monolayer thickness, mm		0.12
Tensile strength, MPa 25℃	GOST R 56785	2135
Tensile modulus of elasticity, GPa 25℃	GOST R 56785	146
Relative elongation at failure, % 25℃	GOST R 56785	1,476
Compressive strength, MPa 25℃	GOST R 56812	1135
Compressive modulus of elasticity, GPa 25℃	GOST R 56812	126
Relative deformation under compression, % 25℃	GOST R 56812	0.864
Interlaminar shear strength, MPa 25℃	GOST 32659	89.7
Interlaminar shear strength, MPa 85℃	GOST 32659	66.6
Shear strength in a plane, MPa 25℃	GOST R 56799	-
In-plane shear strength, MPa 85℃	GOST R 56799	39
Density, g/cm3	GOST 15139	1.52

Prepreg VNT120T/UD120