Prepreg epoxy T107/22502/UMT42S-3K

Tensile strength, MPa

96
Bending strength, MPa

193
Glass transition temperature Tg , °C

175
Crack resistance GIC, J•m2

1452
Crack resistance KIC, MPa•m1/2

2,119
T hole, °C

180
Operating temperature, °C

120
Type of binder

Epoxy
Reinforcing filler

carbon fabric twill 2/2 200 g/m2, UMT42S-3K
Width, mm

1000

from 13 500 ₽/m²

excluding VAT

from 16 470 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

T107 is a prepreg based on an epoxy binder and carbon reinforcing filler (unidirectional tapes or fabrics of various weaves) for the manufacture of parts operated at temperatures up to 120 °C.

Applies:

from 13 500 ₽/m²

excluding VAT

from 16 470 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

The material is included in the register of industrial products of the State Register of Industrial Product Specifications of the Ministry of Industry and Trade of Russia

Other epoxy - curing 180°c

T hole, °C:
180
Operating temperature, °C:
120
Type of binder:
Epoxy
Reinforcing filler:
carbon tape 120 g/m2
Width, mm:
1000

T hole, °C:
180
Operating temperature, °C:
120
Type of binder:
Эпоксидный, 35%
Reinforcing filler:
углеродная лента 195 г/м2
Width, mm:
1000

T hole, °C:
180
Operating temperature, °C:
120
Type of binder:
Epoxy
Reinforcing filler:
carbon fabric twill 2/2 200 g/m2, ITA40-3K
Width, mm:
1000

T hole, °C:
180
Operating temperature, °C:
120
Type of binder:
Epoxy
Reinforcing filler:
fiberglass T-64-(VMP)-78
Width, mm:
920

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

+7 (495) 133-26-78

for product purchasing inquiries

sales@itecma.ru

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

info@cspekt.ru

production and warehouse

Podolsk, Zavodskaya St., Building 2

head office

Moscow, Ramensky Boulevard, Building 1

Website creation – NetLab

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Compressive strength, MPa at 25°C	807
Compressive strength, MPa at 70°C wet.	617
Compressive modulus of elasticity, GPa at 25°C	58
Expansive strength, MPa at 25°C	911
Modulus of elasticity during expansion, GPa at 25°C	71
Shear strength, MPa at 25°C	80
Shear strength, MPa at 70°C wet.	62
Shear strength, MPa at 120°C	56
Compressive strength after impact 6.67 J/mm, MPa	300

Prepreg epoxy T107/22502/UMT42S-3K