Prepreg epoxyphenol ITM180T/UD200

Monolayer thickness, mm

0.19
Tensile strength σ11+, MPa at 25°C

2067
Tensile modulus of elasticity E11+, GPa at 25°C

150
Compressive strength σ11-, MPa at 25°C

994
Shear strength τ13, MPa at 25°C

81
T hole, °C

130℃ (120 min)/150℃ (10 min)
Operating temperature, °C

85
Type of binder

Epoxyphenolic
Reinforcing filler

200g/m2 carbon unidirectional tape

from 4 900 ₽/m²

excluding VAT

from 5 978 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

Epoxy-phenolic prepreg ITM180T is used for the production of aircraft floor panels and for lining cargo and baggage compartments.

Applies:

from 4 900 ₽/m²

excluding VAT

from 5 978 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

Other prepregs

T hole, °C:
130℃ (120 min)/150℃ (10 min)
Operating temperature, °C:
85
Type of binder:
Epoxyphenolic
Reinforcing filler:
carbon unidirectional tape 160 g/m2

T hole, °C:
130℃ (120 мин)/150℃ (15 мин)
Operating temperature, °C:
85
Type of binder:
Эпоксифенольный
Reinforcing filler:
стеклоткань Э3/1-100, 100 г/м²

T hole, °C:
130℃ (120 мин)/150℃ (10 мин)
Operating temperature, °C:
85
Type of binder:
Эпоксифенольный
Reinforcing filler:
углеродная однонаправленная лента 120 г/м2

T hole, °C:
130℃ (120 min)/150℃ (15 min)
Operating temperature, °C:
85
Type of binder:
Epoxyphenolic
Reinforcing filler:
carbon fabric 200 g/m2

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

+7 (495) 133-26-78

for product purchasing inquiries

sales@itecma.ru

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

info@cspekt.ru

production and warehouse

Podolsk, Zavodskaya St., Building 2

head office

Moscow, Ramensky Boulevard, Building 1

Website creation – NetLab

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Charring length, avg., mm	60
Burning time, avg., sec	1
Burning of a drop separating from a test sample after falling on average, avg., sec	0

Monolayer thickness, mm	GOST R 56682	0.19
Tensile strength σ11+, MPa at 25°C	GOST R 56785	2067
Tensile modulus of elasticity E11+, GPa at 25°C	GOST R 56785	150
Compressive strength σ11-, MPa at 25°C	GOST 56812	994
Shear strength τ13, MPa at 25°C	GOST 32659	81
Shear strength τ13, MPa at 85°C	GOST 32659	59

Prepreg epoxyphenol ITM180T/UD200

Key Features

Scope of application