Epoxy-phenolic prepreg ITM180T/UD140

Monolayer thickness, mm

0.14
Tensile strength σ11+, MPa at 25°C

2015
Tensile modulus of elasticity E11+, GPa at 25°C

150
Compressive strength σ11-, MPa at 25°C

1020
Shear strength τ13, MPa at 25°C

78
T hole, °C

130℃ (120 min)/150℃ (10 min)
Operating temperature, °C

85
Type of binder

Epoxyphenolic
Reinforcing filler

carbon unidirectional tape 140 g/m2

from 4 100 ₽/m²

excluding VAT

from 5 002 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

Epoxy-phenolic prepreg ITM180T is used for the production of aircraft floor panels and for lining cargo and baggage compartments.

Applies:

from 4 100 ₽/m²

excluding VAT

from 5 002 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

Other prepregs

T hole, °C:
130℃ (120 min)/150℃ (10 min)
Operating temperature, °C:
85
Type of binder:
Epoxyphenolic
Reinforcing filler:
200g/m2 carbon unidirectional tape

T hole, °C:
130℃ (120 мин)/150℃ (15 мин)
Operating temperature, °C:
85
Type of binder:
Эпоксифенольный
Reinforcing filler:
стеклоткань Э3/1-100, 100 г/м²

T hole, °C:
130℃ (120 мин)/150℃ (10 мин)
Operating temperature, °C:
85
Type of binder:
Эпоксифенольный
Reinforcing filler:
стеклоткань С280, 280 г/м2

T hole, °C:
130℃ (120 min)/150℃ (15 min)
Operating temperature, °C:
85
Type of binder:
Epoxyphenolic
Reinforcing filler:
carbon fabric 200 g/m2

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

+7 (495) 133-26-78

for product purchasing inquiries

sales@itecma.ru

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

info@cspekt.ru

production and warehouse

Podolsk, Zavodskaya St., Building 2

head office

Moscow, Ramensky Boulevard, Building 1

Website creation – NetLab

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Monolayer thickness, mm	GOST R 56682	0.14
Tensile strength σ11+, MPa at 25°C	GOST R 56785	2015
Tensile modulus of elasticity E11+, GPa at 25°C	GOST R 56785	150
Compressive strength σ11-, MPa at 25°C	GOST 56812	1020
Shear strength τ13, MPa at 25°C	GOST 32659	78
Shear strength τ13, MPa at 85°C	GOST 32659	55
In-plane shear strength τ12, MPa at 25°C	GOST R 56799	59
In-plane shear strength τ12, MPa at 85°C	GOST R 56799	48
Tensile strength [+45/0/-45/90]3S, σ11+, MPa at 25°C	GOST R 56785	658
Tensile modulus [+45/0/-45/90]3S, E11+, GPa at 25°C	GOST R 56785	54
Compressive strength [+45/0/-45/90]3S, σ12-, MPa at 25°C	GOST 56812	521
Shear strength [+45/0/-45/90]3S, τ13, MPa at 25°C	GOST 32659	58
Shear strength [+45/0/-45/90]3S, τ13, MPa at 85°C	GOST 32659	42
In-plane shear strength [+45/0/-45/90]3S, τ12, MPa at 25°C	GOST R 56799	294
In-plane shear strength [+45/0/-45/90]3S, τ12, MPa at 85°C	GOST R 56799	242

Charring length, avg., mm	60
Burning time, avg., sec	1
Burning of a drop separating from a test sample after falling on average, avg., sec	0

Epoxy-phenolic prepreg ITM180T/UD140

Key Features

Scope of application