Epoxy binder TO200

Tensile strength, MPa

60
Tensile modulus, GPa Limit bending strength, MPa

94
Crack resistance, KIC, MPa ∙ m1/2

0.639
Strain energy, GIC, J/m2

223
Glass transition temperature, Tg, °С

211
Impregnation temperature, °C

25
Viscosity

no more than 500 mPa s at 25°C
T hole, °C

25-190
Operating temperature, °C

190

from 4 950 ₽/kg

excluding VAT

from 6 039 ₽/kg

with 22% VAT

Minimum order quantity -

10 kg. (A+B)

Not a public offer

The binder can be used both for the production of parts from PCM based on carbon or glass fibers, resistant to elevated operating temperatures up to 120°C, and for the production of composite equipment for operation up to 190°C.

Supply kit

Components A and B are supplied in metal buckets.

10 and 20 liters.

Applies:

from 4 950 ₽/kg

excluding VAT

from 6 039 ₽/kg

with 22% VAT

Minimum order quantity -

10 kg. (A+B)

Not a public offer

Other epoxy resins

Impregnation temperature, °C:
70
Viscosity:
no more than 100 mPa s at 70°C
T hole, °C:
180
Operating temperature, °C:
140

Impregnation temperature, °C:
180
Viscosity:
no more than 78 mPa s at 110°C
T hole, °C:
180
Operating temperature, °C:
150

Impregnation temperature, °C:
25
Viscosity:
no more than 400 mPa s at 25°C
T hole, °C:
25-80
Operating temperature, °C:
80

Impregnation temperature, °C:
40
Viscosity:
не более 150 мПа·с при 25°С
T hole, °C:
50
Operating temperature, °C:
50

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

+7 (495) 133-26-78

for product purchasing inquiries

sales@itecma.ru

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

info@cspekt.ru

production and warehouse

Podolsk, Zavodskaya St., Building 2

head office

Moscow, Ramensky Boulevard, Building 1

Website creation – NetLab

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Carbon fabric 22502 (2x2 twill, 200 g/m2)
Tensile strength at 0°σ11+, MPa at 25°C	ASTM D3039	814
Tensile modulus 0°E11+, GPa at 25°C	ASTM D3039	61
Compressive strength 0° σ11-, MPa at 25°C	ASTM D6641	602
Modulus of elasticity at 0° E11- compression, GPa at 25°C	ASTM D695	59
Shear strength τ13 , MPa at 25°C	ASTM D2344	65
Shear strength τ13 , MPa at 80°C	ASTM D2344	48
Tensile strength with shear τ13, MPa at 120°C	ASTM D2344	34
Shear strength τ12 max (5%), MPa at 25°C	ASTM D5379	113(82)
Shear modulus of elasticity G12, GPa at 25°C	ASTM D5379	3.34