Epoxy binder T20-60

Tensile Strength, MPa

80
Tensile Modulus, GPa

3.2
Glass Transition Temperature Tg (E´´), °С

87
Elongation at break, %

4.6
Flexural strength, MPa

155

2 000 ₽/kg

excluding VAT

2 440 ₽/kg

with 22% VAT

Minimum order quantity -

10 kg.

Not a public offer

The binder exhibits low viscosity at impregnation temperatures (25°C) and cures at room temperature. T20-60 allows for the production of low-porosity polymer composite materials with optimal mechanical properties.

Binder T20-60 is supplied as a set (A+B) in plastic canisters of 10 and 5 liters.

10 kg

7.6 kg A+ 2.4 kg B
20 kg

7.6 kg A and 7.6 kg A and 4.8 kg B
20 kg

7.6 kg A and 7.6 kg A and 2.4 kg B and 2.4 kg B

Applies:

2 000 ₽/kg

excluding VAT

2 440 ₽/kg

with 22% VAT

Minimum order quantity -

10 kg.

Not a public offer

Other epoxy resins

Impregnation temperature, °C:
40
Viscosity:
не более 150 мПа·с при 25°С
T hole, °C:
50
Operating temperature, °C:
50

Impregnation temperature, °C:
70
Viscosity:
no more than 100 mPa s at 70°C
T hole, °C:
180
Operating temperature, °C:
140

Impregnation temperature, °C:
25
Viscosity:
no more than 350 mPa s at 25°C
T hole, °C:
25-190
Operating temperature, °C:
190

Impregnation temperature, °C:
40-70
Viscosity:
no more than 400 mPa s at 40°C
T hole, °C:
140
Operating temperature, °C:
150

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

+7 (495) 133-26-78

for product purchasing inquiries

sales@itecma.ru

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

info@cspekt.ru

production and warehouse

Podolsk, Zavodskaya St., Building 2

head office

Moscow, Ramensky Boulevard, Building 1

Website creation – NetLab

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Tensile strength, MPa	ASTM D638	80
Tensile modulus of elasticity, GPa	ASTM D638	3.2
Glass transition temperature Tg (E´´), °С	ASTM D790	87
Elongation at break, %	ASTM D5045	4.6
Bending strength, MPa	ASTM D5045	155
Crack resistance, KIC, MPa*m1/2	ASTM E2092	0.763
Strain energy, GIC, J/m2	ASTM D792	386

Carbon fabric 22502 (2x2 twill, 200 g/m2, carbon thread UMT42S-3K-EP)
Tensile strength at 0° σ11+, MPa at 25°C	GOST R 56785	957
Tensile modulus of elasticity at 0° E11+, GPa at 25°C	GOST R 56785	64
Compressive strength 0° σ11-, MPa at 25°C	GOST R 56812	645
Compressive strength 0° σ11-, MPa at 80°C	GOST R 56812	460
Compression modulus of elasticity at 0° E11-, GPa at 25°C	GOST R 56812	63
Compression modulus of elasticity 0° E11+, GPa at 80°C	GOST R 56812	56
Interlaminar shear strength τ13, MPa at 25°C	GOST 32659	62
Interlaminar shear strength τ13, MPa at 80°C	GOST 32659	36
Shear strength in the sheet plane τ12 (destruction), MPa at 25°C	GOST 32659	110
Shear modulus G12, GPa at 25°C	GOST 56799	4.1
Shear modulus of elasticity G12, GPa at 80°C	GOST 56799	2.5

Epoxy binder T20-60

Key Features