Epoxy prepreg C107/T-10-14

Surface density of fabric, g/m2

290
Monolayer thickness, mm

0.24
Width, mm

920
Tensile strength, MPa

620
Shear strength, MPa

73.9
T hole, °C

180
Operating temperature, °C

120
Type of binder

Epoxy
Reinforcing filler

fiberglass T-10-14(92)

from 3 364 ₽/m²

excluding VAT

from 4 104 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

C107 is a prepreg based on an epoxy binder and glass reinforcing filler (glass fabric T-10-14(92), T-64(VMP)-78) for the manufacture of parts operated at temperatures up to 120 °C.

Applies:

from 3 364 ₽/m²

excluding VAT

from 4 104 ₽/m²

with 22% VAT

Minimum order quantity -

50 m²

Not a public offer

The material is included in the register of industrial products of the State Register of Industrial Product Specifications of the Ministry of Industry and Trade of Russia

Other epoxy - curing 180°c

T hole, °C:
180
Operating temperature, °C:
120
Type of binder:
Epoxy
Reinforcing filler:
fiberglass T-64-(VMP)-78
Width, mm:
920

T hole, °C:
180
Operating temperature, °C:
120
Type of binder:
Epoxy
Reinforcing filler:
carbon fabric twill 2/2 200 g/m2, UMT42S-3K
Width, mm:
1000

T hole, °C:
180
Operating temperature, °C:
120
Type of binder:
Эпоксидный, 35%
Reinforcing filler:
углеродная лента 195 г/м2
Width, mm:
1000

T hole, °C:
180
Operating temperature, °C:
150
Type of binder:
Epoxy
Reinforcing filler:
carbon twill fabric 2/2 200 g/m2
Width, mm:
1000

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

+7 (495) 133-26-78

for product purchasing inquiries

sales@itecma.ru

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

info@cspekt.ru

production and warehouse

Podolsk, Zavodskaya St., Building 2

head office

Moscow, Ramensky Boulevard, Building 1

Website creation – NetLab

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Tensile strength, MPa	96
Bending strength, MPa	193
Glass transition temperature Tg, °C	175
Crack resistance Gic, J/m2	1452
Moisture saturation 52h boiling water, %	3.5
Glass transition temperature, wet Tg, °C	153

Tensile strength, MPa at 25°	GOST R 56785	620
Tensile modulus of elasticity, GPa at 25°	GOST R 56785	29
Tensile strength, MPa at 70°	GOST R 56785	593
Tensile modulus of elasticity, GPa at 70°	GOST R 56785	28.7
Compressive strength, MPa at 25°	GOST R 56812	656
Compressive modulus of elasticity, GPa at 25°	GOST R 56812	27.7
Compressive strength, MPa at 70°	GOST R 56812	550
Compressive modulus of elasticity, GPa at 70°	GOST R 56812	27.9
Shear strength, MPa at 25°	GOST 32659	73.9
Shear strength, MPa at 70°	GOST 32659	65.2
Shear strength, MPa at 120°	GOST 32659	54.4

Epoxy prepreg C107/T-10-14

Storage and transportation