Resins

Description and benefits

  • In-house developed polymeric resins for mass and high-tech industries.
  • Resins line for tooling.

The line of ITECMA resins is well balanced for various applications, operating temperatures and methods of manufacturing (like vacuum infusion, RTM, winding and manual lamination).

The polymeric matrix (resin) allocates the load between the fibers of the reinforcing filler. The resin is responsible for composite specifications, such as mechanical strength especially the shear and compression strength, operating temperature and moisture absorption.

The major specification of a resin is its processability - the operability in manufacturing.The processability of a resin is described by an impregnation temperature, viscosity at the infusion moment, pot life and a temperature of pre- and post-сuring.

Tooling resins
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
SB322
The binder is designed for the production of of PCM by methods of vacuum infusion and injection in mold ТУ 2257-054-59846689-2016
  • carbon fabric, 200 g/m2,
  • 2x2 twill weave
185 -60/+250 230
Operating temperature up to 80 °С
Material Cur temp, °C Num of components Imp temp, °C Post-Cur temp, °C Viscosity Tg, °C Usage
T20-60
ТУ 2257-053-59846689-2016
25 2 25 80 not more than 400 mPa-s at 25°C 87 Binder for the production of PCM by winding methods, manual lamination, RTM and vacuum infusion
Operating temperature up to 150 °С
Material Cur temp, °C Num of components Imp temp, °C Post-Cur temp, °C Viscosity Tg, °C Usage
T20-60
ТУ 2257-053-59846689-2016
25 2 25 80 not more than 400 mPa-s at 25°C 87 Binder for the production of PCM by winding methods, manual lamination, RTM and vacuum infusion
Material Reinforcing filler Surface density, g/m2 Cur temp, °C Oper temp, °C
KP-120
PCM-PKM and metal-to-metal bonding ТУ 20.16.40-078-59846689-2018
reinforced with non-woven material 300±20 180 180
Material Cur temp, °C Num of components Imp temp, °C Post-Cur temp, °C Viscosity Tg, °C
T26
ТУ 2257-017-59846689-2021
180 1 100 - not more than 78 mPa-s at 120°C 202
Material Reinforcing filler Surface density, g/m2 Cur temp, °C Oper temp, °C
B180
Vacuum forming, thermocompression, pressing and autoclave molding TU 1916-065-59846689-2017
carbon fabric twill 2x2 weave (200 g/m2) 315±30 180 120
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
SB 332
The binder is designed for the production of of PCM by methods of vacuum infusion and injection in mold ТУ 2257-054-59846689-2016
binder with a viscosity less than 200cP at 120°C 190 -60/+250 230
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
PB-250
Filling of honeycomb panels for their local hardening under the fastening elements ТУ 2257-050-59846689-2016
paste with a density of 0.65 g/cm3 185 -60/+250 230
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
M250
Autoclave molding, thermocompression and pressing TU 23.99.14-074-59846689-2018
  • carbon fabric, 200 g/m2,
  • 2x2 twill weave
185 -60/+250 230
Material Reinforcing filler Surface density, g/m2 Cur temp, °C Oper temp, °C
T107
Thermal compression, compression and autoclave molding ТУ 1916-066-59846689-2017 ТУ 23.99.14-016-73047899-2021
  • углеродная ткань саржевого плетения 2х2 (200 г/м2 и 280 г/м2)
  • однонаправленная углеродная лента (120 г/м2 и 200 г/м2)
  • 330±20
  • 450±20
  • 190±20
  • 300±20
180 120
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
SB322
The binder is designed for the production of of PCM by methods of vacuum infusion and injection in mold ТУ 2257-054-59846689-2016
  • carbon fabric, 200 g/m2,
  • 2x2 twill weave
185 -60/+250 230
Operating temperature up to 250 °С
Material Cur temp, °C Num of components Imp temp, °C Post-Cur temp, °C Viscosity Tg, °C Usage
T20-60
ТУ 2257-053-59846689-2016
25 2 25 80 not more than 400 mPa-s at 25°C 87 Binder for the production of PCM by winding methods, manual lamination, RTM and vacuum infusion
Material Reinforcing filler Surface density, g/m2 Cur temp, °C Oper temp, °C
KP-120
PCM-PKM and metal-to-metal bonding ТУ 20.16.40-078-59846689-2018
reinforced with non-woven material 300±20 180 180
Material Cur temp, °C Num of components Imp temp, °C Post-Cur temp, °C Viscosity Tg, °C
T26
ТУ 2257-017-59846689-2021
180 1 100 - not more than 78 mPa-s at 120°C 202
Material Reinforcing filler Surface density, g/m2 Cur temp, °C Oper temp, °C
B180
Vacuum forming, thermocompression, pressing and autoclave molding TU 1916-065-59846689-2017
carbon fabric twill 2x2 weave (200 g/m2) 315±30 180 120
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
SB 332
The binder is designed for the production of of PCM by methods of vacuum infusion and injection in mold ТУ 2257-054-59846689-2016
binder with a viscosity less than 200cP at 120°C 190 -60/+250 230
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
PB-250
Filling of honeycomb panels for their local hardening under the fastening elements ТУ 2257-050-59846689-2016
paste with a density of 0.65 g/cm3 185 -60/+250 230
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
M250
Autoclave molding, thermocompression and pressing TU 23.99.14-074-59846689-2018
  • carbon fabric, 200 g/m2,
  • 2x2 twill weave
185 -60/+250 230
Material Reinforcing filler Surface density, g/m2 Cur temp, °C Oper temp, °C
T107
Thermal compression, compression and autoclave molding ТУ 1916-066-59846689-2017 ТУ 23.99.14-016-73047899-2021
  • углеродная ткань саржевого плетения 2х2 (200 г/м2 и 280 г/м2)
  • однонаправленная углеродная лента (120 г/м2 и 200 г/м2)
  • 330±20
  • 450±20
  • 190±20
  • 300±20
180 120
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
SB322
The binder is designed for the production of of PCM by methods of vacuum infusion and injection in mold ТУ 2257-054-59846689-2016
  • carbon fabric, 200 g/m2,
  • 2x2 twill weave
185 -60/+250 230
Operating temperature up to 450 °С
Material Cur temp, °C Num of components Imp temp, °C Post-Cur temp, °C Viscosity Tg, °C Usage
T20-60
ТУ 2257-053-59846689-2016
25 2 25 80 not more than 400 mPa-s at 25°C 87 Binder for the production of PCM by winding methods, manual lamination, RTM and vacuum infusion
Material Reinforcing filler Surface density, g/m2 Cur temp, °C Oper temp, °C
KP-120
PCM-PKM and metal-to-metal bonding ТУ 20.16.40-078-59846689-2018
reinforced with non-woven material 300±20 180 180
Material Cur temp, °C Num of components Imp temp, °C Post-Cur temp, °C Viscosity Tg, °C
T26
ТУ 2257-017-59846689-2021
180 1 100 - not more than 78 mPa-s at 120°C 202
Material Reinforcing filler Surface density, g/m2 Cur temp, °C Oper temp, °C
B180
Vacuum forming, thermocompression, pressing and autoclave molding TU 1916-065-59846689-2017
carbon fabric twill 2x2 weave (200 g/m2) 315±30 180 120
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
SB 332
The binder is designed for the production of of PCM by methods of vacuum infusion and injection in mold ТУ 2257-054-59846689-2016
binder with a viscosity less than 200cP at 120°C 190 -60/+250 230
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
PB-250
Filling of honeycomb panels for their local hardening under the fastening elements ТУ 2257-050-59846689-2016
paste with a density of 0.65 g/cm3 185 -60/+250 230
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
M250
Autoclave molding, thermocompression and pressing TU 23.99.14-074-59846689-2018
  • carbon fabric, 200 g/m2,
  • 2x2 twill weave
185 -60/+250 230
Material Reinforcing filler Surface density, g/m2 Cur temp, °C Oper temp, °C
T107
Thermal compression, compression and autoclave molding ТУ 1916-066-59846689-2017 ТУ 23.99.14-016-73047899-2021
  • углеродная ткань саржевого плетения 2х2 (200 г/м2 и 280 г/м2)
  • однонаправленная углеродная лента (120 г/м2 и 200 г/м2)
  • 330±20
  • 450±20
  • 190±20
  • 300±20
180 120
Material Reinforcing filler Cur temp, °C Oper temp, °C Post-Cur temp, °C
SB322
The binder is designed for the production of of PCM by methods of vacuum infusion and injection in mold ТУ 2257-054-59846689-2016
  • carbon fabric, 200 g/m2,
  • 2x2 twill weave
185 -60/+250 230