Epoxy binder T40-140

Tensile strength, MPa

87
Tensile modulus of elasticity, GPa

3.2
Elongation at break, %

3.5
Bending strength, MPa

155
Flexural modulus of elasticity, GPa

3.6
Impregnation temperature, °C

40-70
Viscosity

no more than 400 mPa s at 40°C
T hole, °C

140
Operating temperature, °C

150

from 5 700 ₽/kg

excluding VAT

from 6 954 ₽/kg

with 22% VAT

Minimum order quantity -

10 kg

Not a public offer

Epoxy binder T40-140 with a low impregnation temperature (40°C) makes it possible to manufacture PCM products with low porosity and high physical and mechanical characteristics.

Applies:

from 5 700 ₽/kg

excluding VAT

from 6 954 ₽/kg

with 22% VAT

Minimum order quantity -

10 kg

Not a public offer

Other epoxy resins

Impregnation temperature, °C:
25-40
Viscosity:
no more than 500 mPa s at 25°C
T hole, °C:
25-120
Operating temperature, °C:
100

Impregnation temperature, °C:
25
Viscosity:
no more than 400 mPa s at 25°C
T hole, °C:
25-80
Operating temperature, °C:
80

Impregnation temperature, °C:
25
Viscosity:
no more than 350 mPa s at 25°C
T hole, °C:
25-190
Operating temperature, °C:
190

Impregnation temperature, °C:
70
Viscosity:
no more than 100 mPa s at 70°C
T hole, °C:
180
Operating temperature, °C:
140

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

+7 (495) 133-26-78

for product purchasing inquiries

sales@itecma.ru

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

info@cspekt.ru

production and warehouse

Podolsk, Zavodskaya St., Building 2

head office

Moscow, Ramensky Boulevard, Building 1

Website creation – NetLab

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Carbon fabric 22502 (2x2 twill, 200 g/m2, carbon fiber UMT42S-3K-EP)
Tensile strength at 0° σ11+, MPa at 25°C	GOST R 56785	850
Tensile modulus at 0° E11+, GPa at 25°C	GOST R 56785	70
Shear strength τ13, MPa at 25°C	GOST 32659	74
Compressive strength at 0° σ11-, MPa at 25°C	GOST 56812	770
Modulus of elasticity at 0° compression E11-, GPa at 25°C	GOST 56812	64
Compressive strength at 0° σ11-, MPa at 85°C wet	GOST 56812	650
Modulus of elasticity at 0° E11- compression, GPa at 85°C wet	GOST 56812	63

Carbon unidirectional tape 10524 (200 g / m2, carbon fiber UMT49S-12K)
Tensile strength at 0° σ11+, MPa at 25°C	GOST R 56785	2170
Tensile modulus at 0° E11+, GPa at 25°C	GOST R 56785	138
Shear strength τ13, MPa at 25°C	GOST 32659	74
Compressive strength at 0° σ11-, MPa at 25°C	GOST R 56812	1030
Modulus of elasticity at 0° compression E11-, GPa at 25°C	GOST R 56812	126
Compressive strength at 0° σ11-, MPa at 85°C wet	GOST R 56812	730
Modulus of elasticity at 0° E11- compression, GPa at 85°C wet	GOST R 56812	63

Epoxy binder T40-140

Features and Benefits

Recommended conditions of use