Epoxy binder TK123

Tensile strength, MPa

80
Tensile modulus of elasticity, GPa

3.56
Elongation at break, %

3.4
Glass transition temperature Tg, °C

140
Density of cured binder, g/cm3

1,137

3 900 ₽/kg

excluding VAT

4 758 ₽/kg

with 22% VAT

Minimum order quantity -

10 kg.

Not a public offer

The binder has low viscosity at room temperature (less than 500 MPa • s at 25 °C), which makes it possible to obtain polymer composite materials with low porosity and high physical and mechanical characteristics.

TK123 binder is supplied as a set (A+B) in 20-liter metal buckets.

20 kg

14.0 kg A and 6.0 kg B

Applies:

3 900 ₽/kg

excluding VAT

4 758 ₽/kg

with 22% VAT

Minimum order quantity -

10 kg.

Not a public offer

Other epoxy resins

Impregnation temperature, °C:
40
Viscosity:
не более 150 мПа·с при 25°С
T hole, °C:
50
Operating temperature, °C:
50

Impregnation temperature, °C:
25
Viscosity:
no more than 350 mPa s at 25°C
T hole, °C:
25-190
Operating temperature, °C:
190

Impregnation temperature, °C:
25
Viscosity:
272 mPa s
T hole, °C:
25
Operating temperature, °C:
до 80

Impregnation temperature, °C:
25
Viscosity:
no more than 400 mPa s at 25°C
T hole, °C:
25
Operating temperature, °C:
до 80

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

+7 (495) 133-26-78

for product purchasing inquiries

sales@itecma.ru

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

info@cspekt.ru

production and warehouse

Podolsk, Zavodskaya St., Building 2

head office

Moscow, Ramensky Boulevard, Building 1

Website creation – NetLab

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Carbon fabric 22502 (2x2 twill, 200 g/m2, carbon fiber UMT-42S-3K)
Shear strength, MPa at 25°C	EN2563	64
Shear strength, MPa at 80°C wet	EN2563	52
Compressive strength, MPa at 25°C	ASTM D6641	768
Compressive modulus of elasticity, GPa at 25°C	ASTM D695	64
Tensile strength, MPa at 25°C	ASTM D6641	979

Tensile strength, MPa	80
Tensile modulus of elasticity, GPa	3.56
Elongation at break, %	3.4
Glass transition temperature Tg, °C	140
Density of cured binder, g/cm3	1,137

Epoxy binder TK123

Key Benefits

Properties of PCM