Structural binder T26

Tensile strength, MPa

95
Elastic modulus, GPa

3.1
Tensile strength in bending, MPa

152
Dry glass transition temperature, Tg, °С

202
Crack resistance, KIC, MPa ∙ m1/2

0.624
Impregnation temperature, °C

180
Viscosity

no more than 78 mPa s at 110°C
T hole, °C

180
Operating temperature, °C

150

from 6 363 ₽/kg

excluding VAT

from 7 763 ₽/kg

with 22% VAT

Minimum order quantity -

10 kg.

Not a public offer

A structural one-component epoxy resin designed for the manufacture of highly loaded structures.

The T26 binder, together with the Robolen carbon tape, has passed the general qualification (passportization) in accordance with the Aviation Regulations and Airworthiness Standards.

Supply kit

Metal bucket with a capacity of 10 liters.

10 kg.

Applies:

from 6 363 ₽/kg

excluding VAT

from 7 763 ₽/kg

with 22% VAT

Minimum order quantity -

10 kg.

Not a public offer

Other epoxy resins

Impregnation temperature, °C:
25
Viscosity:
no more than 400 mPa s at 25°C
T hole, °C:
25-80
Operating temperature, °C:
80

Impregnation temperature, °C:
25
Viscosity:
no more than 350 mPa s at 25°C
T hole, °C:
25-190
Operating temperature, °C:
190

Impregnation temperature, °C:
40-70
Viscosity:
no more than 400 mPa s at 40°C
T hole, °C:
140
Operating temperature, °C:
150

Impregnation temperature, °C:
40
Viscosity:
не более 150 мПа·с при 25°С
T hole, °C:
50
Operating temperature, °C:
50

Made in Russia

Our goal is to provide our customers with world-class materials and technical support.

phone

+7 (495) 133-26-78

for product purchasing inquiries

sales@itecma.ru

vacancies

hr@itecma.ru

For inquiries regarding the manufacturing of PCM products and tooling, please send an email

info@cspekt.ru

production and warehouse

Podolsk, Zavodskaya St., Building 2

head office

Moscow, Ramensky Boulevard, Building 1

Website creation – NetLab

ITEKMA websites use cookies and other similar technologies. If you continue to browse our website after reading this message, it means you agree to our use of these technologies.

Carbon fiber fabric (CF) and PCF fabric (8H satin, 200g/m2, 3K)		CF	PCF
Tensile strength 0°σ11+, MPa at 25°C	ASTM D3039	910	904
Tensile strength 90°σ22+, MPa at 25°C	ASTM D3039	881	904
Tensile modulus of elasticity 0°E11+, GPa at 25°C	ASTM D3039	65	66
Tensile modulus of elasticity 90°E22+, GPa at 25°C	ASTM D3039	66	66
Compressive strength at 0° σ11-, MPa at 25°C	ASTM D6641	643	638
Compressive strength at 90° σ22-, GPa at 25°C	ASTM D6641	679	608
Shear strength τ13, MPa at 25°C	ASTM D2344	74	66
Ultimate shear strength τ13, MPa at 120°C	ASTM D2344	51	40
Ultimate shear strength τ13, MPa at 150°C	ASTM D2344	45	34
Ultimate shear strength τ12, MPa at 25°C	ASTM D3518	84	79
Shear elastic modulus G12, GPa at 25°C	ASTM D3518	4.5	4.3
Compression after impact 6.67 J/mm, MPa	ASTM D7137	225	301
Delamination area, mm2	ASTM D7137	679	483
Deformation energy GIC, kJ/m2	ASTM D5528	0.4-0.5	0.8-2.8

Carbon fiber unidirectional tape with veil 11424 (200 g/m2, 12K)
Compressive strength at 0°σ11+, MPa	ASTM D3039	1886
Compressive strength at 0° σ11-, MPa at 25°С	ASTM D6641	1210
Compressive strength at 0° σ11-, MPa at 80°С	ASTM D6641	920
Compressive strength 0° σ11-, MPa at 120°C	ASTM D6641	772
Strength at compression 0° σ11-, MPa at 150°C Limit tensile strength 90° σ22+, MPa	ASTM D3039	59
Compressive strength 90° σ22-, MPa	ASTM D6641	166
Tensile modulus of elasticity 0° E11+, GPa	ASTM D3039	108
Elastic modulus at tensile strength 90° E22+, GPa	ASTM D3039	7.0
Shear strength τ13, MPa at 25°C	ASTM D2344	69
Shear strength τ13 , MPa at 80°С	ASTM D2344	46
Shear strength τ13 , MPa at 120°С	ASTM D2344	34
Ultimate shear strength τ13, MPa at 150°C	ASTM D2344	28
Strength at shear τ12, MPa	ASTM D3518	80
Shear modulus of elasticity G12, GPa	ASTM D3518	4.0
Compression after impact 6.67 J/mm, MPa	ASTM D7137	340

Structural binder T26

Features and Benefits

Recommended processing conditions